Título: Effect of surface treatment of fiberglass posts on bond strength to root dentin
Autor: Valdivia, Andréa Dolores Correia Miranda
Novais, Veridiana Resende
Menezes, Murilo de Sousa
Roscoe, Marina Guimarães
Estrela, Carlos
Soares, Carlos José
Resumo: Este estudo avaliou a influência de tratamentos de superfície de pinos de fibra de vidro na resistência de união à dentina radicular por meio do teste de push-out. Quarenta raízes de incisivos bovinos foram submetidas a tratamento endodôntico. A superfície dos pinos de fibra de vidro (Exacto #2, Angelus) foram tratadas com 4 protocolos diferentes (n=10): Controle - 70 % de etanol durante 1 min; 37 % de ácido fosfórico durante 1 min, 10% de ácido fluorídrico durante 1 min e 24 % de peróxido de hidrogênio durante 1 min. Depois foi aplicado agente de união silano por 1 min e todos os pinos foram cimentados com cimento resinoso auto-adesivo (RelyX Unicem, 3M- ESPE). As raízes foram seccionadas e foram obtidas duas fatias de 1 mm de espessura em cada terço: cervical, médio e apical. Os espécimes foram submetidos ao teste de push-out com uma velocidade de 0.5 mm/min. Os dados foram analisados pelo teste ANOVA com medidas repetidas, seguido pelo teste de Tukey HSD (α=0,05). Os fatores tratamento de superfície (p<0,001) e região do terço radicular (p=0,007) foram significantes; no entanto, a interação entre os dois fatores não foi significante (p=0,827). A retenção ao canal radicular foi afetada pelo tipo de tratamento de superfície. O tratamento de superfície com 24% de peróxido de hidrogênio por 1 min rendeu significativamente maior resistência de união quando os pinos de fibra de vidro foram cimentados com RelyX Unicem.
Abstract: his study evaluated the influence of the surface treatments of fiberglass posts on bond strength to root dentin using push-out test. Forty bovine incisor roots were endodontically treated. The surface of the fiberglass posts (Exacto #2, Angelus) were treated using 4 different protocols (n=10): Control - 70% ethanol for 1 min; 37% phosphoric acid for 1 min; 10% hydrofluoric acid for 1 min; and 24% hydrogen peroxide for 1 min. After a silane coupling agent was applied for 1 min and all posts were cemented using self-adhesive resin cement (RelyX Unicem, 3M-ESPE). The roots were sectioned and two 1-mm-thick slices were obtained from each third: cervical, middle and apical. The specimens were subjected to the push-out test with a crosshead speed of 0.5 mm/min. Data were analyzed by repeated measures ANOVA followed by Tukey's HSD tests (α=0.05). The surface treatment (p<0.001) and root third region (p=0.007) factors were significant. The retention to root canal was affected by surface treatment type. The post surface treatment with 24% hydrogen peroxide for 1 min yielded significantly higher bond strength when the fiberglass posts were cemented with RelyX Unicem.
Palavras-chave: Surface treatments
Fiberglass posts
Push-out test
Self-adhesive resin cement
País: Brasil
Unidade acadêmica: Faculdade de Odontologia - FO (RG)
Citação: VALDIVIA, Andréa Dolores Correia Miranda et al. Effect of surface treatment of fiberglass posts on bond strength to root dentin. Brazilian Dental Journal, Ribeirão Preto, v. 25, n. 4, p. 314-320, 2014.
Tipo de acesso: Acesso Aberto
Identificador do documento: 10.1590/0103-6440201300143
Identificador do documento: 10.1590/0103-6440201300143
URI: http://repositorio.bc.ufg.br/handle/ri/16455
Data de publicação: 2014
Aparece nas coleções:FM - Artigos publicados em periódicos

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Artigo - Andréa Dolores Correia Miranda Valdivia - 2014.pdf1,2 MBAdobe PDFThumbnail
Baixar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons