Título: Antimicrobial and chemical study of MTA, Portland cement, calcium hydroxide paste, Sealapex and Dycal
Autor: Estrela, Carlos
Bammann, Lili Luschke
Estrela, Cyntia Rodrigues de Araújo
Silva, Reginaldo Santana da
Pecora, Jesus Djalma
Resumo: O objetivo deste estudo foi investigar a ação antimicrobiana do agregado trióxido mineral (MTA), cimento Portland, pasta de hidróxido de cálcio (CHP), Sealapex e Dycal. Os elementos químicos do MTA e de dois cimentos Portland também foram analisados. Quatro cepas bacterianas: Staphylococcus aureus (ATCC 6538), Enterococcus faecalis (ATCC 29212), Pseudomonas aeruginosa (ATCC 27853), Bacillus subtilis (ATCC 6633), um fungo, Candida albicans (ICB/USP-562), e uma mistura destes foram usados. Trinta placas de Petri com 20 ml de BHI agar foram inoculadas com 0,1 ml da suspensão experimental. Três cavidades, cada uma medindo 4 mm de profundidade e 4 mm de diâmetro, foram feitas em cada placa usando um cilindro de cobre e, em seguida, completamente preenchidas com os produtos a serem testados. As placas foram pré-incubadas por 1 h em temperatura ambiente e, a seguir, incubadas a 37°C por 48 h. Os diâmetros das zonas de inibição microbiana e de difusão foram medidos. Amostras dos halos de difusão e inibição foram extraídos de cada placa e imersos em 7 ml de caldo BHI e incubados a 37°C por 48 h. A análise química dos elementos presentes no MTA e em duas amostras de cimentos Portland foi feita com um Espectrômetro de Fluorecência de Raios-X. Os resultados mostraram que a atividade antimicrobiana da pasta de hidróxido de cálcio foi superior a todas as outras substâncias (MTA, cimento Portland, Sealapex e Dycal), sobre todos os microrganismos testados, apresentando zonas de inibição com 6-9,5 mm e zonas de difusão com 10-18 mm. O MTA, o cimento Portland e o Sealapex apresentaram somente zonas de difusão e, dentre estes, o Sealapex apresentou a maior zona. O Dycal não apresentou halos de inibição, nem de difusão. Os cimentos Portland contém os mesmos elementos químicos que o MTA, com a exceção que o MTA também apresenta, na sua constituição, o bismuto.
Abstract: The objective of this study was to investigate the antimicrobial action of mineral trioxide aggregate (MTA), Portland cement, calcium hydroxide paste (CHP), Sealapex and Dycal. The chemical elements of MTA and two Portland cements were also analyzed. Four standard bacterial strains: Staphylococcus aureus (ATCC 6538), Enterococcus faecalis (ATCC 29212), Pseudomonas aeruginosa (ATCC 27853), Bacillus subtilis (ATCC 6633), one wild fungus, Candida albicans (ICB/USP-562), and one mixture of these were used. Thirty Petri plates with 20 ml of BHI agar were inoculated with 0.1 ml of the experimental suspensions. Three cavities, each one measuring 4 mm in depth and 4 mm in diameter, were made in each agar plate using a copper coil and then completely filled with the product to be tested. The plates were pre-incubated for 1 h at environmental temperature followed by incubation at 37°C for 48 h. The diameters of the zones of microbial inhibition were then measured. Samples from diffusion and inhibition halos were extracted from each plate and immersed in 7 ml BHI broth and incubated at 37°C for 48 h. Analyses of chemical elements present in MTA and in two samples of Portland cement were performed with a fluorescence spectrometer Rx. The results showed that the antimicrobial activity of CHP was superior to those of MTA, Portland cement, Sealapex and Dycal, for all microorganisms tested, presenting inhibition zones of 6-9.5 mm and diffusion zones of 10-18 mm. MTA, Portland cement, and Sealapex presented only diffusion zones and among these, Sealapex produced the largest zone. Dycal did not show inhibition or diffusion zones. Portland cements contain the same chemical elements as MTA except that MTA also contains bismuth.
Palavras-chave: Calcium hydroxide
Vehicles
Intracanal dressing
País: Brasil
Unidade acadêmica: Faculdade de Odontologia - FO (RG)
Citação: ESTRELA, Carlos et al. Antimicrobial and chemical study of MTA, Portland cement, calcium hydroxide paste, Sealapex and Dycal. Brazilian Dental Journal, Ribeirão Preto v. 11, n. 1, p. 3-9, 2000.
Tipo de acesso: Acesso Aberto
URI: http://repositorio.bc.ufg.br/handle/ri/16497
Data de publicação: 2000
Aparece nas coleções:FM - Artigos publicados em periódicos

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Artigo - Carlos Estrela - 2000.pdf175,4 kBAdobe PDFThumbnail
Baixar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons