Avaliação da capacidade de proteção contra a corrosão da arma-dura induzida por cloretos de concretos com adições minerais e inibidores de corrosão
Carregando...
Arquivos
Data
2009-09-28
Autores
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal de Goiás
Resumo
Increasing the durability of concrete structural elements is primordial, especially those related to power generation in eolic areas that are subjected to the phenomenon of reinforcement corrosion. In this context, this study aims to evaluate the overall protection ability of concrete to the phenomenon of reinforcement corrosion induced by chlorides. To this end, it was adopted a statistical program based on a fractional factorial design in which the variables studied were as follows: the water-binder ratio (0.35, 0.45 and 0.55), the type of mineral admixture (silica fume and blast furnace slag at specific levels), the type of corrosion inhibitor (calcium nitrite, sodium nitrite and amine) and the level of corrosion inhibitor (minimum and maximum recommended by each manufacturer). In the concrete investigations, the tests performed were corrosion potential, polarization resistance and electrochemical impedance. Throughout the experiments, it was possible to testify the beneficial effect of reducing the water-binder ratio. It was also possible to prove the very positive effect of the incorporation of mineral admixtures, especially of silica fume. The satisfactory performance of various inhibitors evaluated was also verified, specially when concrete contains mineral admixtures. A parallel study was conducted to make a comparative analysis of inhibitors at the same range of concentrations (at solid levels of 0.76%, 2.21% and 3.66% of the compound on the cement mass), nevertheless this study have demonstrated that fixing contents for all inhibitor is not appropriated, and the recommended dosages by the manufacturer is the best condition. As the levels recommended by manufacturers, it was found that the higher percentages have not worked well for sodium nitrite otherwise, for amine and nitrite calcium, the higher levels implied better results. Regarding the tannin inhibitor also assessed in the parallel study mentioned above (related to specific inhibitors), its good performance related to corrosion inhibition happened just for the content of 0.76% (the lowest levels). For the other contents, it was verified anomalous results. These results demonstrated that each type of corrosion inhibitor has its optimal concentration for use in concrete. Based on a cost-benefit analysis and evaluating the increase in the concrete value for cubic meter (in R$) in the presence of inhibitors at the same contents, it was verified a relative parity prices among the tested nitrites and an extremely high cost of amine. However, when performing the same analysis but using the levels recommended by the manufacturers for each inhibitor independent, it was found that the large disparity in prices between nitrite and amine was reduced considerably. An assessment of technical and economic feasibility was also performed based on the efficiency of corrosion inhibition and cost per cubic meter of concrete mixtures that did not show a typical depassivation of their stell bar up to the attack age evaluated
Descrição
Citação
LIMA, Marcelo Batista. Evaluation of the ability to protect against corrosion of the gun hard-induced chloride concrete with mineral additions and corrosion inhibitors. 2009. 219 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Goiás, Goiânia, 2009.