Síntese e caracterização de compostos do sistema x/2 Al²O³-x/2 Y²O³ (100 - x) SiO² (x=10,20,30,40 e 50) dopados com Er³+ para aplicação em fotônica
Carregando...
Data
2010-12-15
Autores
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal de Goiás
Resumo
This work is to study the crystallization of compounds in the form of post system alumina-yttria-silica prepared by sol-gel mixed methodology and Pechini. Powders (x / 2) Y ² ³ - (X / 2) Al ² O ³ - (1-x) SiO ² (x = 0.1 0.2, 0.3, 0.4 and 0.5 mol) were doped with erbium prepared and characterized. The physical properties of composite SiO ² ¹ YO-, 5 - AlO ¹, 5 were studied by x-ray diffraction, FTIR spectroscopy, thermogravimetry, differential thermal analysis and photoluminescence measurements. It was possible to maintain the amorphous compositions at high temperatures, no crystallization below 900 ° C and the formation of phase Y ² ² O7 Si at 1100 ° C. We obtained a reasonable life time of some compositions treated at 1000 ° C. We observed the emission of green upconversion to excite the samples with high power laser. All synthesized samples exhibit photoluminescence emission and have maximum emission at 1530 nm with a width of ~ 47nm. This broad issue is a desirable property for amplifiers used in systems division multiplexing wavelengths (WDM) and suggests that Er ³ + ions are hosted in the amorphous phase.
Descrição
Palavras-chave
Citação
OLIVEIRA, Alexandre Miranda de. Synthesis and characterization of the system
x/2 Al²O³-x/2 Y²O³ (100 - x) SiO² (x=10,20,30,40 e 50)
dopados com Er³+ para aplicação em fotônica.. 2010. 97 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de Goiás, Goiânia, 2010.