Caracterização estrutural e magnética do compósito cerâmico ZnO – CoFe2O4
Nenhuma Miniatura disponível
Data
2015-08-12
Autores
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal de Goiás
Resumo
Multiferroic materials that simultaneously exhibit two or more physical properties have increasingly raised the interest of the scientific and technological community to develop new multifunctional materials. The discuss all stages of manufacturing, morphological, structural and magnetic characterization of a multifunctional composite containing zinc oxide and cobalt ferrite. Thus, studies of ZnO, and the CoFe2O4 composite (0,80ZnO+0,20 CoFe2O4) initiated by the synthesis of nanosized powders by combustion reaction phases were performed. The compounds studied were sintered at different temperatures (1100 to 1250°C) to obtain relative density near to 90% of the theoretical density. Analysis by scanning electron microscopy, spectroscopy energy dispersive, vibrating sample magnometry and diffraction ray-X were made. Measurements of magnetic properties were conducted at room temperature (22°C) and high temperature (22°C to 700°C). In the samples, formation of ceramic structures was verified, the stoichiometry of the proposed chemical compounds was maintained and possibly the formation of a mixed zinc and cobalt ferrite to composite samples. In the sample of the composite sintered at 1250°C there was the formation of cubic zinc oxide. The magnetic behavior and magnetic anisotropy of the samples were similar, however, significant differences were observed in the values of the Curie temperature, coercive field, can assume different origins for the magnetic CoFe2O4 and the composite (0,80ZnO+0,20CoFe2O4) due, perhaps to the formation of a mixed ferrite.
Descrição
Citação
Oliveira Neto, F. Caracterização estrutural e magnética do compósito cerâmico ZnO – CoFe2O4. 2015. 91 f. Dissertação (Mestrado em Física) - Universidade Federal de Goiás, Goiânia, 2015.