Antimicrobial and chemical study of MTA, Portland cement, calcium hydroxide paste, Sealapex and Dycal
Carregando...
Data
2000
Título da Revista
ISSN da Revista
Título de Volume
Editor
Resumo
The objective of this study was to investigate the antimicrobial action of mineral trioxide aggregate (MTA),
Portland cement, calcium hydroxide paste (CHP), Sealapex and Dycal. The chemical elements of MTA and
two Portland cements were also analyzed. Four standard bacterial strains: Staphylococcus aureus (ATCC
6538), Enterococcus faecalis (ATCC 29212), Pseudomonas aeruginosa (ATCC 27853), Bacillus subtilis
(ATCC 6633), one wild fungus, Candida albicans (ICB/USP-562), and one mixture of these were used.
Thirty Petri plates with 20 ml of BHI agar were inoculated with 0.1 ml of the experimental suspensions.
Three cavities, each one measuring 4 mm in depth and 4 mm in diameter, were made in each agar plate using
a copper coil and then completely filled with the product to be tested. The plates were pre-incubated for 1 h
at environmental temperature followed by incubation at 37°C for 48 h. The diameters of the zones of
microbial inhibition were then measured. Samples from diffusion and inhibition halos were extracted from
each plate and immersed in 7 ml BHI broth and incubated at 37°C for 48 h. Analyses of chemical elements
present in MTA and in two samples of Portland cement were performed with a fluorescence spectrometer
Rx. The results showed that the antimicrobial activity of CHP was superior to those of MTA, Portland
cement, Sealapex and Dycal, for all microorganisms tested, presenting inhibition zones of 6-9.5 mm and
diffusion zones of 10-18 mm. MTA, Portland cement, and Sealapex presented only diffusion zones and
among these, Sealapex produced the largest zone. Dycal did not show inhibition or diffusion zones. Portland
cements contain the same chemical elements as MTA except that MTA also contains bismuth.